Polyisocyanurate (PIR) is a foaming material made by the polymerization of isocyanate and polyether. With superior physical and fire resistance properties compared to polyurethane, it features small thermal conductivity and high dimensional stability, making it an excellent organic hard thermal insulation material.
| Item | Unit | Technical Data | Test Mode |
|---|---|---|---|
| Density | kg/m3 | ≥40 | ASTM D1622 / ISO 845 |
| Thermal Conductivity | W/(m*K) |
≤0.035 (+100℃) ≤0.029 (+50℃) ≤0.025 (+10℃) ≤0.024 (0℃) ≤0.023 (-50℃) ≤0.022 (-100℃) ≤0.017 (-150℃) ≤0.016 (-170℃) |
ASTM C177 |
| Compressive Strength | kPa |
+23℃: ≥200 -165℃: ≥280 |
ASTM D 1621 |
| Tensile Strength | kPa |
+23℃: ≥320 -165℃: ≥265 |
ASTM D 1623 |
| Flame Spread Index | ﹤25 | ASTM E84 | |
| Oxygen index | ≥30 | GB/T 2406.2 | |
| Water Absorption by Vol. | % | ≤2 | ASTM D2842 |
| Water Vapor Permeability | ng/(Pa*s*m) | ≤5.5 | ASTM E96 |
| Closed Cell Ratio | % | ≥95 | ASTM D6226 |
| Lineal Thermal Expansion Coefficient | m/(m*K) | ≤70×10-6 | ASTM D696 |
| PH Value | 5.5-7 | ASTM C871 | |
| Chloride Content | ppm | ≤60 | GB/T 11835 |
| Elastic Modulus | MPa | ≤16 | ASTM D1623 |
| Service Temp. | ℃ | -196～+120 |
As an ideal organic low-temperature heat insulation material with small thermal conductivity and high dimensional stability, PIR is suitable for a wide temperature range. It is widely used in LNG, ethylene, cold storage and other low-temperature industries.